- : 0086-21-61182423
- : 0086-21-61182425
- : [email protected]
- : Room 301,Unit 6,lane 2500,xiupu Road,Kangqiao Industrial Area,Pudong New District,Shanghai
- Performance that API 5L X52 PSL2 pipeline steel should have
- Surface Quality Requirements of EH40 Steel plate
- Excellent properties and applications of EH40 shipbuilding Steel
- Influence of gas in 50CrMo4 steel plate
- Cause of Quenching Cracks in 50CrMo4
- Factors Affecting Welding Toughness of
- Z direction performance of EH32 steel plate
- Features of AR450 wear-resistant plate
- Characteristics of NM500 wear-resistant plate
- Harm of inclusions in API 5L X42 pipeline steel
201 stainless steel Mechanical Properties,201 stainless steel Chemical Composition
201 stainless steel is a low nickel, high-work hardening, austenitic chromium-nickel-manganese stainless steel. Type 201 is not hardenable by heat treatment. Type 201 may be substituted, in some cases, for other higher nickel content alloys.
201 stainless steel Chemical Composition
Carbon .15 Max
Manganese 5.5 - 7.5
Phosphorus .060 Max
Sulfur .030 Max
Silicon 1.00 Max
Chromium 16.00 - 18.00
Nickel 3.50 - 5.50
Nitrogen .25 Max
Molybdenum
201 stainless steel Mechanical Properties (Annealed, Per ASTM A240)
UTS 75,000 ksi Min
Elongation % in 2" 40.00 Min
Rockwell Hardness RB95.00 Max
201 stainless steel Formability
Type 201 stainless steel is formable to most shapes but will work-harden disallowing the most severe forming operations unless annealed prior to forming.
201 stainless steel Magnetic Properties
Type 201 stainless steel is non-magnetic in the annealed condition but becomes magnetic when cold-worked.